Raw Material Easy to Form Nylon Granules PA66 Pellets with 25% Glass Fiber Reinforced for Extrusion
Product Introduction
-Nylon/PA66 granules reinforced by fiberglass. The performance of final products of this raw material were in line with the national standard.
-The product is based on PA66 resin as basic, add glass fiber, efficient flame retardants and various additives, formed by twin-screw extrusion blending.
Advantage:
- High mechanical strength
- High toughness
- High softening point
- Good wear resistance
- Self-lubrication
- Long-term work at higher temperatures
- It has high CTI value , excellent electrical insulation, low smoke and low toxicity characteristics.
Details of related standard:
- GB/T 23615.1-2009 Accessorial material for architectural aluminum alloy profiles -- Part 1: Thermal barrier strip of polyamide
- EN 14024-2004 Metal profiles with thermal barrier -- Mechanical performance Requirement, proof and tests for assessment
- YS/T 437-2008 Aluminium profiles moment of inertia calculation methods and computing software requirements
- JG/T 174-2005 Thermal barrier strips for construction industry
- GB 5237.6 -2012 Wrought aluminium alloy extruded profiles for architecture -- Part 6: Thermal barrier profiles
- GB/T 8478-2008 Aluminium windows and doors
- GB/T 8484-2008 Graduation and test for thermal insulating properties of doors and windows
- JG 175-2011 Insulating aluminum alloy profiles with thermal barrier for buildings
Polywell PA66 Granules Performance Table
NO. |
Item |
Unit |
GB/T 23615.1-2009 |
PW-Technical specification |
|
Material Properties |
1 |
Density |
g/cm3 |
1.3±0.05 |
1.28-1.35 |
2 |
Linear expansion coefficient |
K-1 |
(2.3-3.5)×10-5 |
(2.3-3.5)×10-5 |
3 |
Vicat softening temperature |
ºC |
≥230ºC |
≥233ºC |
4 |
Melting point |
ºC |
≥240 |
≥240 |
5 |
Testing for tensile cracks |
- |
No cracks |
No cracks |
6 |
Shore hardness |
- |
80±5 |
80-85 |
7 |
Impact strength(Unnotched) |
KJ/m2 |
≥35 |
≥38 |
8 |
Tensile strength(longitudinal) |
MPa |
≥80a |
≥82a |
9 |
Elasticity modulus |
MPa |
≥4500 |
≥4550 |
10 |
Elongation at break |
% |
≥2.5 |
≥2.6 |
11 |
Tensile strength(transverse) |
MPa |
≥70a |
≥70a |
12 |
High temperature tensile strength(transverse) |
MPa |
≥45a |
≥47a |
13 |
Low temperature tensile strength(transverse) |
MPa |
≥80a |
≥81a |
14 |
Water resistance tensile strength(transverse) |
MPa |
≥35a |
≥35a |
15 |
Aging resistance tensile strength(transverse) |
MPa |
≥50a |
≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
About color:
The color of our products is black, but we also can customize according to customers' requirements.
Application:
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 7-15 working days after payment.
Our Company
Related Products we can provide:
Thermal Break Strip Extruding Machine |
Thermal Break Strip |
Extrusion Mold |
Please feel free to contact us if you have any questions.
Address: Jinfeng Town, Zhangjiagang City, Jiangsu Province, China