Nylon Polyamide 66 Glass Fiber 25% Plastic Raw Material Granules for Extruding Broken Bridge Thermal Break Strips

• Customization: Available
• Feature: High Mechanic Strength
• CAS No.: 32131-17-2
• Model NO.: PW-PA66GF25
• Formula: [C12h22n2o2]N
• Material: Granules
• Usage: Engineerina Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Product Catefories: Glass Fiber Reinforced Plastic
• Technical Performance: GB/T 23615.1-2009
• Certificates: SGS
• Fiber Type: Gfrp
• Applied: PA Thermal Break Strips
• Raw Material: PA66, Fiberglass
• UV Resistant: Yes
• Certificate: SGS
• Transport Package: Woven Bags
• Specification: 25kg/bag
• Trademark: Polywell
• Origin: Zhangjiagang, China
• HS Code: 3908101190
• Production Capacity: 20 Tons Per Day

Product Description

Nylon Polyamide 66 Glass Fiber 25% Plastic Raw Material Granules for Extruding Broken Bridge Thermal Break Strips
Product Introduction
-Nylon/PA66 granules reinforced by fiberglass. The performance of final products of this raw material were in line with the national standard.
-The product is based on PA66 resin as basic, add glass fiber, efficient flame retardants and various additives, formed by twin-screw extrusion blending.
  
Polywell PA66 Granules Performance Table 

NO.	Item	Unit	GB/T 23615.1-2009	PW-Technical specification
	Material Properties
1	Density	g/cm^3	1.3±0.05	1.28-1.35
2	Linear expansion coefficient	K^-1	(2.3-3.5)×10^-5	(2.3-3.5)×10^-5
3	Vicat softening temperature	ºC	≥230ºC	≥233ºC
4	Melting point	ºC	≥240	≥240
5	Testing for tensile cracks	-	No cracks	No cracks
6	Shore hardness	-	80±5	80-85
7	Impact strength(Unnotched)	KJ/m^2	≥35	≥38
8	Tensile strength(longitudinal)	MPa	≥80^a	≥82^a
9	Elasticity modulus	MPa	≥4500	≥4550
10	Elongation at break	%	≥2.5	≥2.6
11	Tensile strength(transverse)	MPa	≥70^a	≥70^a
12	High temperature tensile strength(transverse)	MPa	≥45^a	≥47^a
13	Low temperature tensile strength(transverse)	MPa	≥80^a	≥81^a
14	Water resistance tensile strength(transverse)	MPa	≥35^a	≥35^a
15	Aging resistance tensile strength(transverse)	MPa	≥50^a	≥50^a

1.Sample water content less than 0.2% by weight.

2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
   
 Our Company
Related Products we can provide

Thermal Break Strip Extruding Machine

Thermal Break Strip

Granulator Machine

Please feel free to contact us if you have any questions.

Address: Jinfeng Town, Zhangjiagang City, Jiangsu Province, China