Plastic Raw Material Glass Fiber Reinforced PA66 Granules Polyamide Nylon Compound Pellet

Product Description

Plastic Raw Material Glass Fiber Reinforced PA66 Granules Polyamide Nylon Compound for Thermal Break Strip

Product Introduction:
Polyamide 6.6 granules reinforced by fiberglass, with special additives, is blended and extruded by twin screw extrusion machine. It is more suitable for extrusion of heat insulation strip. Compared with ordinary granules, it is more conducive to forming. It has certain advantages in speed, surface finish and yield. The performances of nylon insulating strip produced made of this material meet the national standards. It can not only be customized according to customer requirements, far exceeding the national standard, but also can add high-efficiency flame retardant to achieve the purpose of flame retardant.
 

Advantage:

1. High mechanical strength
2. High toughness
3. High softening point
4. Good wear resistance
5. Self-lubrication
6. Long-term work at higher temperatures
7. It has high CTI value , excellent electrical insulation, low smoke and low toxicity characteristics.

 

Details of related standard:

• GB/T 23615.1-2009 Accessorial material for architectural aluminum alloy profiles -- Part 1: Thermal barrier strip of polyamide
• EN 14024-2004 Metal profiles with thermal barrier -- Mechanical performance Requirement, proof and tests for assessment
• YS/T 437-2008 Aluminium profiles moment of inertia calculation methods and computing software requirements
• JG/T 174-2005 Thermal barrier strips for construction industry
• GB 5237.6 -2012 Wrought aluminium alloy extruded profiles for architecture -- Part 6: Thermal barrier profiles
• GB/T 8478-2008 Aluminium windows and doors
• GB/T 8484-2008 Graduation and test for thermal insulating properties of doors and windows
• JG 175-2011 Insulating aluminum alloy profiles with thermal barrier for buildings

 
Polywell PA66 Granules Performance Table 

NO.	Item	Unit	GB/T 23615.1-2009	PW-Technical specification
	Material Properties
1	Density	g/cm^3	1.3±0.05	1.28-1.35
2	Linear expansion coefficient	K^-1	(2.3-3.5)×10^-5	(2.3-3.5)×10^-5
3	Vicat softening temperature	ºC	≥230ºC	≥233ºC
4	Melting point	ºC	≥240	≥240
5	Testing for tensile cracks	-	No cracks	No cracks
6	Shore hardness	-	80±5	80-85
7	Impact strength(Unnotched)	KJ/m^2	≥35	≥38
8	Tensile strength(longitudinal)	MPa	≥80^a	≥82^a
9	Elasticity modulus	MPa	≥4500	≥4550
10	Elongation at break	%	≥2.5	≥2.6
11	Tensile strength(transverse)	MPa	≥70^a	≥70^a
12	High temperature tensile strength(transverse)	MPa	≥45^a	≥47^a
13	Low temperature tensile strength(transverse)	MPa	≥80^a	≥81^a
14	Water resistance tensile strength(transverse)	MPa	≥35^a	≥35^a
15	Aging resistance tensile strength(transverse)	MPa	≥50^a	≥50^a

1.Sample water content less than 0.2% by weight.

2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
 
About color:
The color of our products is black, but we also can customize according to customers' requirements.

Application:
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
 
Packaging & Delivery:
Packaging details: 25kg/bag
Delivery details: Shipped in 7-15 working days after payment.

Our Company:

Related Products we can provide:

Thermal Break Strip Extruding Machine

Thermal Break Strip

Extrusion Mold

Please feel free to contact us if you have any questions.

Address: Jinfeng Town, Zhangjiagang City, Jiangsu Province, China